BASA 2K EP-0110
Two-component epoxy primer for priming of steel, aluminum, galvanized surfaces in industrial and marine atmospheres.
One-component universal primer for deep penetration based on polyacrylic resin. It is intended for priming of mineral, including concrete and reinforced concrete, and other non-metallic surfaces as part of coating systems.
Increases the adhesion of the subsequent layers in the coating system.
It is perfectly combined with any types of primers and finishing paintwork materials, including with organic-based materials.
Fire-explosion-proof, does not contain toxic components.
| Technical specifications | |
| Type |
Two-component epoxy primer with high content of dry matter. Can be applied with a large thickness of a dry layer on vertical surfaces. Is used in painting systems, as well as an independent coating. It is delivered in sets: primer basis and hardener. |
| Hardener | 1,5 ± 0,1 |
| Relative viscosity at a temperature of 20±2oC by the VZ-246 viscometer with a nozzle diameter 4 mm, not less | 40-80 |
| Non-volatile matter content, not less % | 58±2 |
| Color | Grey and others upon request |
| Glossiness | Matt (ISO 2813/60º) |
| Consumption, g/m2 |
0.170 The practical consumption is influenced by the quality of a surface, a way and conditions of application, a form of the painted surface. |
| Solvent | Basa Solvent 2K EP |
| Way of application |
Air spraying, airless spraying. A long pile brush or roller at strip painting. |
| Drying time at a temperature of +20oC and relative humidity of 65%, hours | 4 |
| Instruction for use | |
| Conditions of applying |
Temperature of air, the painted surface and primer shouldn't be lower than +5ºС. Temperature of a surface should be at least 3ºС higher than an air dew point. Relative humidity of air should be about 70%. |
| Surface preparation |
The surface must be dry and cleaned of oil, inorganic salts, dirt and dust. Steel. Blasting to a degree not less than Sa 2½ (ISO8501-1.2007). Surface coated: clean, dry and undamaged compatible primer. |
| Method of application |
Before application, carefully mix the primer throughout the container. To be applied with spraying, brush or roller at strip painting. Airless spraying. Pressure on the nozzle 15 MPa, nozzle size 0.43-0.79 mm, spray angle 40 - 80° |
| Recommended paint systems |
Система окраски по металлу 2К ЭП-0111Ц, 2К ЭП-0110, 2К ПУ-110 |
| Tools cleaning | Upon work completion, the painting equipment and tools should be washed out with a recommended solvent |
| More information | |
| Occupational & industrial safety |
Before application it is necessary to study attentively the text and precautionary designations on factory labels. Use in well-ventilated rooms. Do not inhale dust. Avoid contacts with skin. In case of skin and eye exposure, immediately rinse with water and see a doctor. |
| Storage |
The primer should be stored and transported at a temperature not less than minus 10ºС and not higher than plus 30ºС. The primer should be stored in the dry, cool, well-ventilated room, away from heat sources. Package containing the primer and the hardener should be tightly closed. Do not allow freezing during transporting and storage. Shelf life of primer base and hardener (semi-finished products) is not less than 12 months. |
The Scientific Research Institute of Transport Construction was established in 1935, in 1993 it was transformed into a joint-stock company.
All these years, ZNIIS JSC provides reliability and security of construction and operation of complex and unique facilities.
The standard of the Institute is absence of complaints and unconditional fulfillment of obligations. That's why a significant part of our customers cooperate with ZNIIS JSC for years and decades. Since 2002 it has been accredited by TÜV (Germany) in accordance with ISO 9001 standard.
The institute has specialized laboratories and professionals in the field of certification of new building materials, corrosion protection, vibration protection, calculations and physical modeling of complex structures, testing of materials and structures.